The methods for preparing high-purity tantalum target materials by powder metallurgy mainly include hot pressing, hot isostatic pressing, cold isostatic pressing and vacuum sintering, etc. The process flow is: raw material → film → cold isostatic pressing → vacuum sintering → rolling → Annealing→machining→finished product, or directly after hot isostatic pressing to obtain the finished product.
In terms of raw material selection, due to the high oxygen content of tantalum powder, which exceeds 1000μg/g, the vacuum sintering ability to deoxidize is limited. Therefore, the key to this method is to select high-purity, ultra-fine powder as raw material and rapid densification. Sintering technology to ensure the low porosity of the target material, and the preparation process strictly controls the introduction of impurity elements. Some studies have proposed that by nitriding the surface of metal powder, tantalum powder with an oxygen content of less than 300μg/g and a nitrogen content of 10μg/g can be obtained, and then put into the mold, and then subjected to cold pressing and hot isostatic pressing Molding or other sintering methods can obtain a tantalum target with a purity of 99.95% or more, an average grain size of less than 50μm, or even 10μm, random texture, and uniform texture on the surface and thickness of the target. The tantalum target prepared by the powder smelting method has a grain size of less than 60μm and a dense structure, in which the (100) texture is 7.25%, the (110) texture is 13.9%, the (111) texture is 21.7%, and the three textures The composition of the structure is relatively consistent, and there is no strong phenomenon of (111) texture, which meets the requirements of sputtering.
Isostatic pressing is to place the sample to be pressed in a high-pressure container, and use the incompressible property of the liquid medium and the property of uniformly transmitting pressure to uniformly pressurize the sample from all directions, so that the force of the tantalum powder in all directions is uniform. So as to ensure the consistency of the internal structure of the tantalum billet. Then the billet is vacuum sintered. By limiting the degree of vacuum, temperature and time, the impurities in the tantalum billet can be volatilized to the maximum, the original pores disappear, and a denser and higher-purity billet can be obtained, with a relative density of 99.65%. . The unique feature of powder metallurgy is that the powder is pressed into a block by mechanical external force, and then through sintering, the mechanical bond between the pressed powder particles becomes a metal bond bond, which becomes a metal raw material. In this process, the original powder The small grain size and the small degree of grain growth during the sintering process make the grain size of the billet much smaller than the grain size of the smelting ingot, and the grain size can be guaranteed to be less than 60 μm. At the same time, the billet prepared by the powder smelting method has a uniform structure due to the same forming conditions at all positions of the billet, which is far better than the melting structure. The purpose of pressure processing in the later stage is only for forming. There is only one pressure processing process by rolling, which has little effect on the texture. Therefore, the three texture components (100), (111) and (110) can be obtained uniformly. There is no tantalum target with strong (111) texture. However, the current gas impurity content control is still difficult.
Guest contributors are welcome at the Alloy Wiki.It is a weekly wiki and guide on alloy information and processing technology, while also about the vast array of opportunities that are present in manufacturing. Our team of writers consists of a Machining Material Supplier / Machinist / Tool and Die Maker, a Biomedical Engineer / Product Development Engineer, a Job Development Coordinator / Adjunct Professor, and a President and CEO of a manufacturing facility.
Link to this article：High-purity tantalum sputtering target’s preparation by powder metallurgy
Reprint Statement: If there are no special instructions, all articles on this site are original. Please indicate the source for reprinting:Alloy Wiki，thanks